DINITROL 4941 UNDERBODY CHASSIS RUST PROOFING WAX 500ml 4x AEROSOL + CANGUN 1116301 DIN1

Kit Includes 4 x 4941 500ML + Can gun

DINITROL 4941 / 4941 CAR is a long term protective product. The product leaves a firm, black film with short drying time and good adhesion and flexibility on all metal surfaces, rubber and plastic parts.
Benefits
OEM references
Robust universal film
Self-healing
Easily applied
Good abrasion resistance
Component protection
Applications
DINITROL 4941 / 4941 CAR is an underbody product or use in the treatment of vehicles during production, at import plants and in aftermarket applications. When applied to a clean, dry surface, it adheres to both painted surfaces and those coated with a layer of PVC or similar material. Zinc, rubber and plastics are completely unharmed by the product.
A clean and economic treatment on the line is assured by the product‘s ease of application and high dry matter content. DINITROL 4941 / 4941 CAR is also designed for use on spare parts, machines and iron and steel structures in highly corrosive environment. DINITROL 4941 / 4941 CAR is also very suitable as an anticorrosive coating for transport and warehousing under extremely corrosive conditions.
Method of use
DINITROL 4941 / 4941 CAR can be applied by manual or automatic application equipment, airless or airmix.
Recommended application and product temperature is 15 – 30°C.
Pre-treatment Substrates
DINITROL 4941 / 4941 CAR can be applied directly to clean, dry and corrosion free surfaces.
If corrosion is present, DINITROL ML or a DINITROL cavity
wax shall be applied before.
Over-Coating / 2-Layer-Application
DINITROL 4941 / 4941 CAR can not be over-painted.
For additional information, please consult DINOL GmbH.
Technical Data
Colour - black
Type of film - hard, waxy
Density at 23°C - approx. 1100 kg/m³
Viscosity at 23°C - 800 mPas
Dry matter content - 69% by weight
Flash point - 36°C
Aromatic content in solvent - 0,5%
Recommended film thickness wet - 700 μm
Recommended layer thickness - 300 – 500 μm
Drying time - 6 – 12 Stunden through dry
Low temperature adhesion - -20°C
Removability - Hydrocarbon solvents
Heat resistance - 130°C
Salt spray resistance, 300 μm - 1500 hours